Product Details
Place of Origin: Henan, China
Brand Name: HT
Model Number: follow
Payment & Shipping Terms
Minimum Order Quantity: 10 cartons
Price: $650.00/cartons 10-99 cartons
Other Names: |
Furan Resin Adhesive Motar |
MF: |
Furan Resin Adhesive Motar |
Classification: |
Other Adhesives |
Main Raw Material: |
Carbon |
Usage: |
Metallurgy |
Type: |
Furan Resin Adhesive Motar |
Compress Strength After Baking: |
>20mpa |
Volume Density After Baking: |
>1.42g/cm3 |
Specific Resistance: |
<65Ωmm2/m |
Product Name: |
Carbon Tamping Paste |
Other Names: |
Furan Resin Adhesive Motar |
MF: |
Furan Resin Adhesive Motar |
Classification: |
Other Adhesives |
Main Raw Material: |
Carbon |
Usage: |
Metallurgy |
Type: |
Furan Resin Adhesive Motar |
Compress Strength After Baking: |
>20mpa |
Volume Density After Baking: |
>1.42g/cm3 |
Specific Resistance: |
<65Ωmm2/m |
Product Name: |
Carbon Tamping Paste |
Cathode Paste Cold Ramming Paste Used in Joints Between Cathode Graphite Blocks Peripheral Seam
Ramming pastes is widely used in aluminum reduction cell, blast furnace, smelting furnace, industrial silicon smelting,ferroalloy furnace and other industrial furnaces. The main purpose, both in the joints between the cathode blocks and in the peripheral seam, is to fill the voids between the prebaked blocks and prevent metal and bath from penetrating the cathode. Leakage of metal and electrolyte damages the cathode and may lead to premature pot failure.
Ramming paste is a critical part of the cathode. Consistent and high-quality ramming paste products installed according to optimised procedures are required to provide a basis for improved operation and longer pot life.
| Property | Unit | Mean value | |
| Volatile Matter | % | <24.0 | |
| Ash | % | <8 | |
| Bulk density | Green mix | g/cm3 | >1.7 |
| Baked mix | >1.55 | ||
| Open porosity | Green paste | % | <5 |
| Baked paste | <18 | ||
| Thermal Conductivity@30ºC | Green paste | W/mK | <6 |
| Baked paste | <8 | ||
| Granularity | mm | <8mm | |
| Max Operaturing Temp. | ºC | 1800 | |