Product Details
Place of Origin: Henan, China
Brand Name: Hong Tai
Model Number: 99,90
Payment & Shipping Terms
Minimum Order Quantity: 2 tons
Price: $1,500.00 - $2,000.00/tons
Packaging Details: 1.Pallet+Paper or Steel angle bead+Paper board +Plastic or Steel belt +Plastic film
(1)Wooden pallet size:Usually0.92*0.92m(standard brick),but 1*1m (special shape brick) at most,
(2)Load weight of each pallet:Usually 1.5-1.7Tons, max 2.0 Tons.
(3
Supply Ability: 3000 Ton/Tons per Month high alumina refractory brick
Shape: |
Brick |
Material: |
Corundum |
SiO2 Content (%): |
0.15%--18.5% |
Al2O3 Content (%): |
80%-99.3% |
MgO Content (%): |
~ |
CaO Content (%): |
~ |
Refractoriness (Degree): |
1770°< Refractoriness< 2000° |
CrO Content (%): |
~ |
SiC Content (%): |
~ |
Processing Service: |
Bending, Welding, Punching, Decoiling, Cutting, Moulding |
Product Name: |
Corundum Brick |
Application: |
Furnace Lining |
Raw Material: |
Alumina |
Color: |
White |
Apparent Porosity/%: |
16%~18% |
Cold Crush Strength MPa: |
>80 |
Bulk Density(g/cm3): |
2.95-3.1 |
Size: |
Customers' Requirement |
Certificate: |
ISO9001-2008 |
Brand: |
Hong Tai |
Shape: |
Brick |
Material: |
Corundum |
SiO2 Content (%): |
0.15%--18.5% |
Al2O3 Content (%): |
80%-99.3% |
MgO Content (%): |
~ |
CaO Content (%): |
~ |
Refractoriness (Degree): |
1770°< Refractoriness< 2000° |
CrO Content (%): |
~ |
SiC Content (%): |
~ |
Processing Service: |
Bending, Welding, Punching, Decoiling, Cutting, Moulding |
Product Name: |
Corundum Brick |
Application: |
Furnace Lining |
Raw Material: |
Alumina |
Color: |
White |
Apparent Porosity/%: |
16%~18% |
Cold Crush Strength MPa: |
>80 |
Bulk Density(g/cm3): |
2.95-3.1 |
Size: |
Customers' Requirement |
Certificate: |
ISO9001-2008 |
Brand: |
Hong Tai |
|
Items
|
Ultra Purity
Corundum brick
|
99 Corundum brick
|
90 Corundum brick
|
Corundum Mullite
Brick
|
|
Al2O3 %
|
≥99.3
|
≥ 98.5
|
≥ 90
|
≥80
|
|
SiO2 %
|
≤0.15
|
≤0.3
|
≤8.5
|
≤18.5
|
|
Fe2O3 %
|
≤0.1
|
≤0.2
|
≤0.2
|
≤0.3
|
|
Bulk density g/cm3
|
≥3.25
|
≥3.25
|
≥3.1
|
≥2.9
|
|
Apparent porosity %
|
≤18
|
≤18
|
≤18
|
≤18
|
|
Cold crushing strength MPa
|
≥100
|
≥100
|
≥100
|
≥100
|
|
Refractoriness under load
(0.2Mpa,0.6%)
|
≥1700
|
≥1700
|
≥1700
|
≥1700
|
|
Reheating linear change rate
(1600℃X 8h)
|
-0.2
|
-0.2
|
0.2
|
0.2
|
|
Thermal expansion %
Tem.to 1300℃
|
8.1
|
8.1
|
8.1
|
7.6
|