Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%

Name: Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%
Brand: HongTai
SKU: HT
Price: 1 USD
Availability: InStock
Rating: 4.8 (124 reviews)

Product Details

Place of Origin: Henan, China

Brand Name: HongTai

Model Number: HT

Payment & Shipping Terms

Minimum Order Quantity: 10 cartons

Price: $1,000.00 - $1,200.00/cartons

Packaging Details: in wooden pallets

Supply Ability: 200000 Carton/Cartons per Month Magnesia Iron Spinel Bricks

Get Best Price

Product Details

Product Description

Highlight:

Shape:	Block	Material:	Alumina Block
SiO2 Content (%):	0.6%	Al2O3 Content (%):	9-12%
MgO Content (%):	87-90%	CaO Content (%):	1.5%
Refractoriness (Degree):	1770°< Refractoriness< 2000°	CrO Content (%):	-
SiC Content (%):	-	Processing Service:	Bending, Welding, Punching, Decoiling, Cutting, Moulding
Bulk Density(g/cm3):	2900-3050kg/m3	Size:	Customized Size
Color:	Yellow	Cold Crushing Strength/Mpa:	55~90
Apparent Porosity/%:	13-16%	Working Temperature:	1600-1900
Name:	Magnesia Iron Spinel Bricks

Shape:	Block
Material:	Alumina Block
SiO2 Content (%):	0.6%
Al2O3 Content (%):	9-12%
MgO Content (%):	87-90%
CaO Content (%):	1.5%
Refractoriness (Degree):	1770°< Refractoriness< 2000°
CrO Content (%):	-
SiC Content (%):	-
Processing Service:	Bending, Welding, Punching, Decoiling, Cutting, Moulding
Bulk Density(g/cm3):	2900-3050kg/m3
Size:	Customized Size
Color:	Yellow
Cold Crushing Strength/Mpa:	55~90
Apparent Porosity/%:	13-16%
Working Temperature:	1600-1900
Name:	Magnesia Iron Spinel Bricks

Long Service Life Periclase Brick Used In Cement Kiln with Apparent Porosity of 13-16%

Details Images

Magnesia Alumina Spinel Brick

It takes good quality fused magnesite and fused mgo-cr clinker as raw material, formed under high pressure,burned in high
temperature. It has character of corrosion resistance.
Main using for VOD,AOD,SKF,LF,RH etc. secondary refining furnace.

Advantage

Products with anti- alkaline corrosion ability, anti-erosion ability, good thermal stability, high strength , less pollution,RUL
advantages

Detail Specification

	FM-MA80	FM-MA85	FM-MA90
MgO %	85	88	90
Al2O3 %	7	6.5	6.5
SiO2 %	4	2.4	1.2
CaO %	1.5	1.3	1.2
Fe2O3 %	1.7	1.4	1.0
Apparent porosity %	17	17	17
Bulk density (g/cm3)	2.93	2.93	2.94
Cold crushing strength (MPa)	50	50	55
Refractoriness under load (°C)	1610	1650	1700
Thermal shock resistance (times)	3-6	3-6	3-6

Standard size: 230 x 114 x 65 mm ,Special size and OEM Service also provide
The size is precise, providing kinds of shapes according to customer's drawing