Product Details
Place of Origin: Henan, China
Brand Name: Hong Tai
Model Number: DMZ
Payment & Shipping Terms
Price: $200.00 - $500.00/tons
Packaging Details: with wooden pallet
Supply Ability: 1000 Ton/Tons per Month Used Magnesia Brick
Shape: |
Brick, Brick Lump |
Material: |
Magnesite |
SiO2 Content (%): |
0.6-4.5% |
Al2O3 Content (%): |
0% |
MgO Content (%): |
91.5-97.5% |
CaO Content (%): |
0-1.6% |
Refractoriness (Degree): |
Super-Class (Refractoriness> 2000°) |
CrO Content (%): |
0.05% |
SiC Content (%): |
0% |
Bulk Density(g/cm3): |
2.9-3.05 |
Application: |
Recycle |
Product Name: |
Used Magnesia Brick |
Apparent Porosity %: |
15-18 |
Cold Crushing Strength(MPa): |
60-80 |
R.U.L: |
1560-1700℃ |
Sample: |
Free |
Packing: |
Standard Exporting Package |
Type: |
Secondhand Refractory Brick |
Port: |
Tianjin |
Shape: |
Brick, Brick Lump |
Material: |
Magnesite |
SiO2 Content (%): |
0.6-4.5% |
Al2O3 Content (%): |
0% |
MgO Content (%): |
91.5-97.5% |
CaO Content (%): |
0-1.6% |
Refractoriness (Degree): |
Super-Class (Refractoriness> 2000°) |
CrO Content (%): |
0.05% |
SiC Content (%): |
0% |
Bulk Density(g/cm3): |
2.9-3.05 |
Application: |
Recycle |
Product Name: |
Used Magnesia Brick |
Apparent Porosity %: |
15-18 |
Cold Crushing Strength(MPa): |
60-80 |
R.U.L: |
1560-1700℃ |
Sample: |
Free |
Packing: |
Standard Exporting Package |
Type: |
Secondhand Refractory Brick |
Port: |
Tianjin |
Used Refractory Magnesia Brick for Recycle
Magnesite brick is an alkaline refractory material with periclase as the main phase.
performance:
Magnesia bricks have high refractoriness, good resistance to alkaline slag, high starting temperature of load softening, but poor thermal shock resistance. The sintered magnesia brick is made of brick magnesia as raw material, and after being pulverized, compounded, kneaded and formed, it is fired at a high temperature of 1550 to 1600 ° C, and the firing temperature of the high-purity product is above 1750 ° C. The non-burned magnesia brick is prepared by adding a suitable chemical binder to the magnesia, mixing, forming and drying.
Uses: Mainly used in glass kiln regenerator lattice brick, cement rotary kiln lining, steelmaking open hearth furnace, electric arc furnace, converter lining, non-ferrous metal smelting furnace, high temperature tunnel kiln, etc.
Used Refractory Magnesia Brick for Recycle