Product Details
Place of Origin: Henan, China
Brand Name: Hong Tai
Model Number: MT5, MT8, MT10, MT12, MT14, MT18
Payment & Shipping Terms
Minimum Order Quantity: 5 tons
Price: $600.00 - $800.00/tons
Packaging Details: Packaging for Magnesia carbon brick
1.Pallet+Paper or Steel angle bead+Paper board +Plastic or Steel belt +Plastic film
(1)Wooden pallet size:Usually0.92*0.92m(standard brick),but 1*1m (special shape brick) at most,
(2) Load weight of each pallet:
Supply Ability: 3000 Ton/Tons per Month high alumina refractory brick
Shape: |
Brick |
Material: |
MgO-Carbon Brick |
SiO2 Content (%): |
Little |
Al2O3 Content (%): |
According To Needs |
MgO Content (%): |
70%-87% |
CaO Content (%): |
Little |
Refractoriness (Degree): |
1770°< Refractoriness< 2000° |
CrO Content (%): |
Little |
SiC Content (%): |
Little |
Processing Service: |
Bending, Welding, Punching, Decoiling, Cutting, Moulding |
Product Name: |
Magnesia Carbon Brick |
Application: |
Ladle,converter, Electric Arc Furnace |
Size: |
Customers' Requirement |
Color: |
Black |
Bulk Density G/cm3: |
2.7-3.05 |
Cold Crush Strength MPa: |
25-45 |
Type: |
Manufacturer |
Feature: |
High Temperature Resistant |
Brand: |
Hong Tai |
Shape: |
Brick |
Material: |
MgO-Carbon Brick |
SiO2 Content (%): |
Little |
Al2O3 Content (%): |
According To Needs |
MgO Content (%): |
70%-87% |
CaO Content (%): |
Little |
Refractoriness (Degree): |
1770°< Refractoriness< 2000° |
CrO Content (%): |
Little |
SiC Content (%): |
Little |
Processing Service: |
Bending, Welding, Punching, Decoiling, Cutting, Moulding |
Product Name: |
Magnesia Carbon Brick |
Application: |
Ladle,converter, Electric Arc Furnace |
Size: |
Customers' Requirement |
Color: |
Black |
Bulk Density G/cm3: |
2.7-3.05 |
Cold Crush Strength MPa: |
25-45 |
Type: |
Manufacturer |
Feature: |
High Temperature Resistant |
Brand: |
Hong Tai |
Item | MT-12A | MT-12B | MT-12C | MT-14A | MT-14B | MT-14C |
MgO | 78 | 76 | 74 | 76 | 74 | 72 |
C | 12 | 12 | 12 | 14 | 14 | 14 |
Apparent porosity/%,<= | 4 | 5 | 6 | 4 | 5 | 6 |
Bulk Density,g/cm3 | 2.98 | 2.96 | 2.95 | 3 | 2.96 | 2.95 |
Crushing Strength/Mpa,>= | 40 | 40 | 35 | 40 | 40 | 35 |
Hot modulus of rupture(1450℃)/Mpa | 8 | 7 | 6 | 12 | 10 | 8 |